In this paper, the effect of intermetallic compounds Zr2Fe and Zr7Ni10 on the microstructure and first hydrogenation kinetic of TiCr1.1V0.9 alloy is reported. Samples were synthesized by arc melting separately and then 5% of each intermetallic was co-melt with TiCr1.1V0.9 alloy. First hydrogenation of all alloys was performed at room temperature under 2.0 MPa of hydrogen. Kinetics and absorption capacities were measured at room temperature, by using apparatus type sieverts. Results indicate that the addition of the intermetallic has an enhancing effect on the kinetic reaction without further modification of hydrogen storage capacities, going from 3.6 wt.% for as-cast alloy, to 3.61 wt.% for alloys +5 wt.% intermetallic. On the other hand, the structure and microstructural analysis were carried out by X-ray diffraction and scanning electron microscopy, respectively. These results show conservation of the structure in the body-centered cubic, and two additional minor phase formations: C14 laves phase for both alloys, and an additional Ti2Ni phase for the TiCr1.1V0.9 + 5% Zr7Ni10 alloy. Finally, the thermal stabilization of the sample was determined by using differential scanning calorimetry. The results show two types of hydrides that form trapped in different clamping sites with different energies.
Heliyon
Universidad de Santander UDES. Vigilada Mineducación.
Resolución otorgada por el Ministerio de Educación Nacional: No. 6216 del 22 de diciembre de 2005 / Personería Jurídica 810 de 12/03/96.
Institución sujeta a inspección y vigilancia por el Ministerio de Educación Nacional. Resolución 12220 de 2016.
Notificaciones administrativas y judiciales:
Copyright © 2021 - Todos los derechos reservados